TY - JOUR
T1 - Novel injectable and in situ curable glycolide/lactide based biodegradable polymer resins and composites
AU - Xie, Dong
AU - Park, Jong Gu
AU - Zhao, Jun
AU - Turner, Charles H.
N1 - Copyright:
Copyright 2009 Elsevier B.V., All rights reserved.
PY - 2007/7
Y1 - 2007/7
N2 - Novel in situ polymerizable liquid three-arm biodegradable oligomeric polyesters based upon glycolic acid (GA), L-lactic acid (LLA), and their copolymers are synthesized and characterized. Injectable and in situ curable polymer neat resins and their composites formulated with bioabsorbable beta-tricalcium phosphate are prepared at room temperature using photo- and redox-initiation systems, respectively. The cured neat resins show the initial compressive yield strength (YCS, MPa), modulus (M, MPa), ultimate compressive strength (UCS, MPa), and toughness (T, kN mm), ranging from 4.0 to 20.1, 201.5 to 730.2, 82.7 to 310.5, and 1.02 to 3.93. The cured composites show the initial YCS, M, UCS and T, ranging from 27.7 to 56.4, 1440 to 4870, 81.6 to 158.9, and 0.94 to 1.97. Increasing GA/LLA ratio increases all the initial compressive strengths of both neat resins and composites. Increasing filler content increases YCS and M but decreases UCS and T. A diametral tensile strength test shows the same trend as a compressive strength test. There seems to be an optimal flexural strength for the composite at the filler content around 43%. An increasing molar ratio increases curing time but decreases the degree of conversion (DC). An increasing filler content increases curing time but decreases exotherm and DC. During the course of degradation, all the materials show a burst degradation behavior within 24 h, followed by an increase in CS. The poly(glycolic acid) neat resin completely loses its strength at around Day 45. The composites completely lose their strengths at different time intervals, depending on their molar ratio and filler content. The degradation rate is found to be molar ratio and filler-content dependent.
AB - Novel in situ polymerizable liquid three-arm biodegradable oligomeric polyesters based upon glycolic acid (GA), L-lactic acid (LLA), and their copolymers are synthesized and characterized. Injectable and in situ curable polymer neat resins and their composites formulated with bioabsorbable beta-tricalcium phosphate are prepared at room temperature using photo- and redox-initiation systems, respectively. The cured neat resins show the initial compressive yield strength (YCS, MPa), modulus (M, MPa), ultimate compressive strength (UCS, MPa), and toughness (T, kN mm), ranging from 4.0 to 20.1, 201.5 to 730.2, 82.7 to 310.5, and 1.02 to 3.93. The cured composites show the initial YCS, M, UCS and T, ranging from 27.7 to 56.4, 1440 to 4870, 81.6 to 158.9, and 0.94 to 1.97. Increasing GA/LLA ratio increases all the initial compressive strengths of both neat resins and composites. Increasing filler content increases YCS and M but decreases UCS and T. A diametral tensile strength test shows the same trend as a compressive strength test. There seems to be an optimal flexural strength for the composite at the filler content around 43%. An increasing molar ratio increases curing time but decreases the degree of conversion (DC). An increasing filler content increases curing time but decreases exotherm and DC. During the course of degradation, all the materials show a burst degradation behavior within 24 h, followed by an increase in CS. The poly(glycolic acid) neat resin completely loses its strength at around Day 45. The composites completely lose their strengths at different time intervals, depending on their molar ratio and filler content. The degradation rate is found to be molar ratio and filler-content dependent.
KW - Biodegradable
KW - Compressive strengths
KW - Degradation
KW - In situ polymerizable
KW - Oligomeric polyesters
UR - http://www.scopus.com/inward/record.url?scp=34447539596&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=34447539596&partnerID=8YFLogxK
U2 - 10.1177/0885328206068691
DO - 10.1177/0885328206068691
M3 - Article
C2 - 16920760
AN - SCOPUS:34447539596
SN - 0885-3282
VL - 22
SP - 33
EP - 54
JO - Journal of Biomaterials Applications
JF - Journal of Biomaterials Applications
IS - 1
ER -